Si 17 TC

Phenolic Based Heat Cured Hydrophobic Lining for Acidic to Weak Alkali Media. Satin Anthracite Finish

SÄKAPHEN Si 17 TC is a high-quality abrasion and impact resistant hydrophobic single-component phenolic based thermosetting heat cured coating, with enhanced permeation resistance (ΔT 65°C). Si 17 TC is self-priming and formulated for direct to metal application.

Si 17 TC is chemically resistant to a variety of mediums ranging from strongly acidic to weakly alkaline aqueous liquids and vapors, fume gases, organic and inorganic acids, chlorinated aromatic and aliphatic hydrocarbons, all types of cooling water including brackish, river and sea water, as well as deionized water, oils and greases. Si 17 TC is also resistant to temperature fluctuations.

The surface contains outstanding hydrophobic properties, preventing caking, fouling and incrustation and once polymerized the lining is fully machinable.

For the coating of ISO Tank Containers, Process Vessels, Pipework, Rotating Equipment and other equipment where exceptional chemical and abrasion resistance as well as enhanced permeation resistance is required.

Product nameUnitSÄKAPHEN® Si 17® TC  
 Properties-Heat Cured Duroplast  
 Resin base-Phenolic resin blend  
 Field of Application-For the coating of ISO tank containers, process vessels, pipe works, rotating equipment and other equipment where excellent chemical resistance as well as abrasion resistance and/or enhanced permeation resistance (Δt < 65°C) is needed..  
 Cure Mechanism-Heat cured  
 Quantity of components-1  
 Color-Anthracite  
 Surface-Satin finished  
 General chemical resistance (All resistances have to be inquired separately!)-Abrasion resistant with enhanced permeation resistance and chemically resistant to various substances ranging from strongly acidic to light alkaline aqueous liquids and vapors, fume gases, organic and inorganic acids, chlorinated aromatic and alphatic hydrocarbons, all types of cooling waters including brackish, river and sea water as well as deionized water, oils and greases.  
 pH RangepH1-8  
 Wet Film Thickness per layerµm100  
 Total dry film thicknessµm180  
 Coverageapprox. kg/m²/DFT1,1 kg / m² / 200µm  
 Surface PreparationSaSA2 ½ - SA 3  
 Surface Profileµm40 - 60 µm  
 Temperature resistance dry (dry air oven)°C-20°C to +180°C/200°C  
 Temperature resistance wet (water)°C-20°C to +180°C/200°C  
 Resistance to water vapor diffusion°C≤ ∆T 65°C  
 Overcoating Waiting Timehours/23°Cno limitations  
 Chemical Curingdaysafter final bake  
 Linear Thermal Expansionµmn/a  
 Pore testingVolts67,5  
 Pendulum hardness acc. to König6° sec153  
 Shore D HardnessShore D95  
 Adhesion TestN/mm² [MPa]>30  
 Salt spray testhours1250  
 Impact Strengthmm (1 kg)> 1000  
 Surface smoothness (Ra)µm
Ø 3 readings
1,27  
 Surface tensionmN/m>38 <41  
 Abrasion resistancemg/1000 r.under examination  
 Crosscutclass   
 Heat conductivity
Ø 12,7x2,0mm on C-Steel with 67,37 w/mK
W/mKn/a  

Combined compatible fillers, based on high-performance ceramics, increase the abrasion and scratch resistance of linings and coatings, simultaneously the chemically inert material group of the ceramics boosts the overall performance of the lining or coating.

SÄKAPHEN Heat Cured Linings and Coatings

High-End Corrosion Protection and Carbon Footprint Reduction

Feel free to contact us for technical advice.

For any specific chemical resistances, fields of use, technical questions or other lining and coating queries, please feel free to contact us for technical advice.

Tel.: +49 20439470 or Email: info[at]saekaphen.de

SÄKAPHEN is happy to support!

 

* Mandatory fields