SÄKAPHEN SÄKAFLAKE 900 Black 3K is a plural-component Novolac Vinyl Ester resin enhanced further by the addition of graphite and glass flakes to provide an electrically conductive (statically dissipative), abrasion resistant lining / coating, offering protection against water vapor diffusion (ΔT 85°C). ). Further, offering chemical resistance against aggressive substances such as acids, salt solvents, flue gases and all types of water including brackish, river, sea water and deionized water.
SÄKAFLAKE 900 Black 3K is specifically formulated and designed to be self-priming for direct to metal application and can be applied on site and on concrete. Upon polymerization the lining is fully machinable and delivers exceptional quality when used for complex structures and fabrications such as Columns where the diameter may be reduced by use of internal baffles or support rings. Bespoke formulation allows for efficient application, even in extreme environmental conditions and has excellent sag resistance allowing for wet on wet application up to 3mm (3000 microns).
SÄKAFLAKE 900 Black 3K is an ultra-high solid / low solvent product with a volume of solid (wt%) of plus 95%. The lining is resistant to temperature fluctuations.
Suitable for the lining or coating of Ancillary Heat Exchanger equipment such as Water Boxes, Channel and Covers, Blowers, Fans, Wash Towers, Process and Storage Tanks, Vessels, Tank Containers, Compressor Casings, assorted Flue Gas Desulfurization equipment including Flue Gas Funnels and Channels. In particular, for equipment requiring water vapor diffusion resistance with high temperature gradients.
|Product name||Unit||SÄKAPHEN® SÄKAFLAKE® 900 Schwarz 3K|
|Properties||-||Cold Cured Duroplast Coating|
|Resin base||-||Novolac Vinyl Ester|
|Field of Application||-||For the coating of chamber parts of heat exchangers, evaporators and air coolers, blowers, fans and compressor casings, flue gas funnels/channels, flue gas desulfurization equipment, wash towers, process and storage tanks, vessels and containers. For equipment requiring a coating resistant to water vapour diffusion also with high temperature gradients and electrical conductivity (electrical surface resistance is less than 10^7Ω).|
|Cure Mechanism||-||Cold Cured Duroplast Coating|
|Quantity of components||-||3|
|General chemical resistance (All resistances have to be inquired separately!)||-||The coating distinguishes itself through high temperature- and diffusion resistance and excellent chemical resistance against aggressive substances such as acids, bases, solvents, salt solvents, fluegas and all types of water, including brackish, river and sea water as well as deionized water.|
|Wet Film Thickness per layer||µm||500 µm|
|Total dry film thickness||µm||1500|
|Coverage||approx. kg/m²/DFT||3,3 kg / m² / 1500µm|
|Surface Preparation||Sa||SA2 ½ - SA 3|
|Temperature resistance dry|
(dry air oven)
|°C||-20°C to +180°C|
|Temperature resistance wet (water)||°C||-20°C to 100°C|
|Resistance to water vapor diffusion||°C||≤ ∆T 85°C|
|Overcoating Waiting Time||hours/23°C||min. 12 hours,|
|Linear Thermal Expansion||µm||n/a|
|Pore testing||Volts||not possible / conductive|
|Pendulum hardness acc. to König||6° sec||n/a|
|Shore D Hardness||Shore D||80|
|Adhesion Test||N/mm² [MPa]||7 - 11|
|Salt spray test||hours||n/a|
|Impact Strength||mm (1 kg)||1 MTH, 450mm, 6 MTH, 750mm (1 kg)|
|Surface smoothness (Ra)||µm|
Ø 3 readings
|Surface tension||mN/m||>44 <48|
|Taber Abrasion resistance, CS17 wheel, 1kg||mg/1000 r.||45|
|Crosscut||class||2 (DIN EN ISO 2409)|
Ø 12,7x2,0mm on C-Steel with 67,37 w/mK
Lamellar carbon fillers containing crystalline structures, comprising two polytype layers, allow simultaneous electrical ablation of the coating whilst maintaining high levels of chemical and water vapor diffusion resistance. The added glass flakes have a reinforcing effect.